Kozlovskiy, A.; Borgekov, D.B.; Zdorovets, M.V.; Kadyrzhanov, K.K.; Shlimas, D.I. Study of Radiation-Induced Damage Processes in CeZrO4–YZrO3 Ceramics Caused by Helium Irradiation. Materials 2023, 16, 198. https://doi.org/10.3390/ma16010198

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...

Giniyatova, S.G.; Kozlovskiy, A.L.; Rspayev, R.M.; Borgekov, D.B.; Zdorovets, M.V. Study of the Kinetics of Radiation Damage in CeO2 Ceramics upon Irradiation with Heavy Ions. Materials 2023, 16, 4653. https:// doi.org/10.3390/ma16134653

Shlimas, D.I.; Borgekov, D.B.; Kadyrzhanov, K.K.; Kozlovskiy, A.L.; Zdorovets, M.V. Study of the Surface-Layer Softening Effects in xLi2ZrO3–(1−x)Li4SiO4 Ceramics under Irradiation with He2+ Ions. Ceramics 2024, 7, 547–561. https://doi.org/10.3390/ ceramics7020036

Kozlovskiy, A.; Borgekov, D.B.; Zdorovets, M.V.; Kadyrzhanov, K.K.; Shlimas, D.I. Study of Radiation-Induced Damage Processes in CeZrO4–YZrO3 Ceramics Caused by Helium Irradiation. Materials 2023, 16, 198. https://doi.org/10.3390/ma16010198

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...

Giniyatova, S.G.; Kozlovskiy, A.L.; Rspayev, R.M.; Borgekov, D.B.; Zdorovets, M.V. Study of the Kinetics of Radiation Damage in CeO2 Ceramics upon Irradiation with Heavy Ions. Materials 2023, 16, 4653. https:// doi.org/10.3390/ma16134653

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...