We present here a novel experimental study of changes after contact electrification in the optical transmission spectra of samples of both pristine and irradiated PET film treated with Kr+15 ions of energy of 1.75 MeV and a fluence of 3 × 1010 cm2 . We used a non-standard electrification scheme for injecting electrons into the film by applying negative electrodes to both its ...

This paper presents a new analysis of the experimental transmission spectra of polyethylene terephthalate (PET) films before and after irradiation with swift heavy ions (SHI) films, as reported previously by the authors. It is shown that the absorption edge red shift for irradiated films contains two regions of exponential form, one of which is located in the UV region and the ...

This paper presents a new analysis of the experimental transmission spectra of polyethylene terephthalate (PET) films before and after irradiation with swift heavy ions (SHI) films, as reported previously by the authors. It is shown that the absorption edge red shift for irradiated films contains two regions of exponential form, one of which is located in the UV region and the ...

This paper presents the results of a study of the ordering in polyethylene terephthalate (PET) film induced by Ar8+ ions with an irradiation fluence of 2 × 1012 ions/cm2 , and of the temporal stability of the induced ordering in the irradiated sample, over a three month period. Immediately after irradiation, sharp new reflections not seen at lower fluences were observed in ...

We report here experimental results investigating the influence of the initial swift heavy ion charge on the structure of polyethylene terephthalate (PET) film after irradiation, using a structurally sensitive X-ray diffraction method. Kr ions with an energy of 100 MeV and charges of 13+, 14+, and 15+ were each used at irradiation fluences of 5 × 1010, 7.5 × 1010, 1 × 1011, ...

This paper presents the results of a study of polyethylene terephthalate (PET) films irradiated with Ar and Kr ions at both normal orientation and an angle of 40◦ to the normal. Normal irradiation was performed using Ar8+ and Kr15+ ions with an energy of 1.75 MeV/au and fluences in the range (2–500) × 1010 cm−2 for Ar8+ ions and (1.6 − 6.5) × 1010 cm−2 for Kr15+ ions. Kr ions ...

We present here a novel experimental study of changes after contact electrification in the optical transmission spectra of samples of both pristine and irradiated PET film treated with Kr+15 ions of energy of 1.75 MeV and a fluence of 3 × 1010 cm2 . We used a non-standard electrification scheme for injecting electrons into the film by applying negative electrodes to both its ...

The novelty of the study is that the ordering that occurs in a PET film under the action of SHI irradiation manifests itself as an increase in the integral intensity of intrinsic luminescence. The Urbach behaviour of the red shift of the absorption edge is used as a baseline for further analysis of experimental optical transmission spectra of PET films irradiated by swift heavy ...