The article outlines findings from a comparative analysis of the effectiveness of doping CeO2 ceramics with a stabilizing additive Y2O3 on alterations in the strength and thermophysical parameters of ceramics under high-temperature irradiation with heavy ions comparable in energy to fission fragments of nuclear fuel, which allows, during high-temperature irradiation, to ...

The article outlines findings from a comparative analysis of the effectiveness of doping CeO2 ceramics with a stabilizing additive Y2O3 on alterations in the strength and thermophysical parameters of ceramics under high-temperature irradiation with heavy ions comparable in energy to fission fragments of nuclear fuel, which allows, during high-temperature irradiation, to ...

Ceramics based on zirconium dioxide are very important compounds for dental, implant, and structural material applications. Despite the fact that tetragonally stabilized YSZ has been well studied, the search for new compositions of zirconia-based ceramics is still in progress. The ZrO2 -CeO2 system is one of the alternatives for YSZ materials, but there is conflicting ...

The paper is devoted to the study of the influence of variation of ZrO2 ceramics grain sizes on the resistance to radiationinduced swelling under irradiation with low-energy Не2+ ions. The choice of ZrO2 ceramics as objects of research is due to high levels of mechanical strength and hardness, as well as low rates of thermal expansion, which eliminates the effects of thermal ...

The aim of this study is to determine the effect of changes in the phase composition of Al2O3–Si3N4 ceramics that were obtained using the method of mechanochemical solid-phase grinding on their resistance to the process of long-term thermal exposure, accompanied by the processes of oxidation and softening. The relevance of this research consists of determining the influence ...

The article outlines findings from a comparative analysis of the effectiveness of doping CeO2 ceramics with a stabilizing additive Y2O3 on alterations in the strength and thermophysical parameters of ceramics under high-temperature irradiation with heavy ions comparable in energy to fission fragments of nuclear fuel, which allows, during high-temperature irradiation, to ...

The aim of this study is to determine the differences in the damaged layer degradation kinetics in two-phase lithium-containing ceramics based on Li2ZrO3 and Li4SiO4 compounds in the case of irradiation with protons and helium ions, simulating the gas swelling and blistering processes, as well as the accumulation of radiolysis products in the damaged layer. During the ...

The study investigates alterations in the mechanical and thermophysical properties of ceramics composed of xLi2ZrO3–(1−x)Li4SiO4 as radiation damage accumulates, mainly linked to helium agglomeration in the surface layer. This research is motivated by the potential to develop lithium-containing ceramics characterized by exceptional strength properties and a resistance to the ...

The paper presents the assessment results of the application of the method of ion modification of the near-surface layer of SiC ceramics in order to create a dislocation hardening effect to enhance the resistance of ceramics to helium swelling and embrittlement. Interest in this topic is due to the possibilities of expanding the practical application of ion modification in the ...

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...