The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...

Zdorovets, M.V.; Borgekov, D.B.; Zhumatayeva, I.Z.; Kenzhina, I.E.; Kozlovskiy, A.L. Synthesis, Properties and Photocatalytic Activity of CaTiO3-Based Ceramics Doped with Lanthanum. Nanomaterials 2022, 12, 2241. https://doi.org/10.3390/ nano12132241

Zdorovets, M.V.; Shlimas, D.I.; Kozlovskiy, A.L.; Borgekov, D.B. Study of the Application Efficiency of Irradiation with Heavy Ions to Increase the Helium Swelling Resistance of BeO Ceramics. Metals 2022, 12, 307. https://doi.org/ 10.3390/met12020307

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...

The aim of this work is to study the effect of lanthanum doping on the phase formation processes in ceramics based on CaTiO3 , as well as to evaluate the effectiveness of the ceramics as photocatalysts for the decomposition of the organic dye Rhodamine B. The methods used were scanning electron microscopy to evaluate the morphological features of the synthesized ceramics, X-ray ...

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...