The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...

The paper is devoted to the study of radiation-induced damage kinetics in beryllium oxide ceramics under irradiation with low-energy helium ions with fluences of 1015–1018 ion/cm2 . It was revealed that at irradiation fluences above 1017 ion/cm2 , a decrease in radiation-induced damage formation and accumulation rate is observed, which indicates the saturation effect. At ...