Аннотации:
This manuscript investigates the enhancement of gas sensing properties of titanium-doped zinc oxide (TZO)
nanostructures using intense pulsed ion beam irradiation (IPIB). TZO nanostructures synthesized using the
sequential ion-layer adsorption and reaction (SILAR) method were subjected to two different treatments: thermal
annealing at 500 ◦C under nitrogen atmosphere and IPIB. The study investigates the morphological, structural,
optical, electrical, and gas-sensing properties of TZO with a focus on the sensitivity and selectivity to nitrogen
monoxide (NO) and other gases. The results show that both annealed (aTZO) and irradiated (iTZO) nanofilms
exhibit enhanced root-mean-square (RMS) roughness, resulting in improved gas sensing performance. IPIB
irradiation induced significant lattice distortions and defects, which played a critical role in the dramatic per
formance improvement of the iTZO sensors. In particular, iTZO demonstrated a remarkable 1300 % improvement
in response to 100 ppm NO at 200 ◦C. Furthermore, Density Functional Theory (DFT) results revealed that NO
gas exhibited a moderate adsorption energy on defective TZO material compared to pristine TZO. This research
demonstrates the effectiveness of IPIB irradiation in improving TZO-based gas sensors, suggesting potential for
environmental monitoring and industrial applications. Future studies may explore the scalability of this tech
nique and its application to other metal oxide semiconductors to develop advanced gas sensors.